Hormigones de alta resistencia con nano-adiciones y fibras de acero

Alizo Mirabal, Manuel Arturo (2015). Hormigones de alta resistencia con nano-adiciones y fibras de acero. Thesis (Master thesis), E.T.S.I. Caminos, Canales y Puertos (UPM).

Description

Title: Hormigones de alta resistencia con nano-adiciones y fibras de acero
Author/s:
  • Alizo Mirabal, Manuel Arturo
Contributor/s:
  • Lucea Martínez, Ildefonso
Item Type: Thesis (Master thesis)
Masters title: Ingeniería de las Estructuras, Cimentaciones y Materiales
Date: 2015
Subjects:
Freetext Keywords: Hormigón de Alta Resistencia, Influencia, Comportamiento, Nano-Sílice, Nano-Alúmina, Fibras de Acero, High Strength Concrete, Behaviour, Nano-Additions, Nano-Silica, Nano-Alumina, Steel Fibers
Faculty: E.T.S.I. Caminos, Canales y Puertos (UPM)
Department: Ingeniería Civil: Construcción
Creative Commons Licenses: Recognition - No derivative works - Non commercial

Full text

[img]
Preview
PDF - Requires a PDF viewer, such as GSview, Xpdf or Adobe Acrobat Reader
Download (4MB) | Preview

Abstract

El presente Trabajo Fin de Máster consistió en determinar la influencia que pueden poseer las nano-adiciones de Sílice y Alúmina y fibras de acero en un Hormigón de Alta Resistencia. Partiendo de una dosificación de Hormigón de Alta Resistencia conocida, que contenía humo de Sílice (10%) y fibras de poliolefina (3kg/m3), se les procedió a sustituir por la incorporación de nano-adiciones de Sílice y Alúmina (7% y 3% respectivamente) y añadiendo fibras de acero en lugar de poliolefina. En el presente trabajo se realizó una campaña experimental de laboratorio, en donde se realizaron tres (3) amasadas de Hormigón de Alta Resistencia con nueve (9) probetas cada una, donde el contenido de nano-adiciones no varió, mientras que el contenido de fibras fue de 20 y 40 kg/m3. Posterior a su realización, se procedió a someter las probetas a ensayos de resistencia a compresión, resistencia a tracción indirecta, resistencia a flexotracción, permeabilidad, módulo de elasticidad y coeficiente de Poisson con el fin de conocer el comportamiento de las amasadas una vez añadidas las nano-adiciones y fibras de acero. Luego de ejecutados los ensayos, se procedió a comparar los resultados entre amasadas y con las del hormigón de referencia. Los resultados muestran que la incorporación de las fibras de acero mejoran las propiedades del Hormigón de Alta Resistencia, sin negatividad. This Master’s Degree Thesis was to determine the influence that steel fibers and nano-additions of Silica and Alumina may possess in a High Strength Concrete mix. Based on a known dosage of High Strength Concrete, which contained Silica fume (10%) and polyolefin fibers (3 kg/m3), they were proceeded to be substituted for the incorporation of nano-additions of Silica and Alumina (7% and 3%, respectively) and by adding steel fibers rather than polyolefin fibers. This thesis carried out an experimental laboratory campaign, in which three (3) mixes of High Strength Concrete had nine (9) specimens each, where the content of nano-additions did not change, while the steel fiber content was 20 and 40 kg/m3. Subsequent to its completion, the specimens were subjected to different tests to determine the compressive strength, tensile strength, flexural strength, permeability, modulus of elasticity and Poisson's ratio in order to know the behavior of the mixes once the nano-additions and steel fibers were added. The results indicate that the steel fibers improve the properties of the High Strength Concrete rather to affect in a negative way

More information

Item ID: 34865
DC Identifier: http://oa.upm.es/34865/
OAI Identifier: oai:oa.upm.es:34865
Deposited by: Biblioteca ETSI Caminos
Deposited on: 07 Apr 2015 09:55
Last Modified: 30 Jul 2015 09:52
  • Logo InvestigaM (UPM)
  • Logo GEOUP4
  • Logo Open Access
  • Open Access
  • Logo Sherpa/Romeo
    Check whether the anglo-saxon journal in which you have published an article allows you to also publish it under open access.
  • Logo Dulcinea
    Check whether the spanish journal in which you have published an article allows you to also publish it under open access.
  • Logo de Recolecta
  • Logo del Observatorio I+D+i UPM
  • Logo de OpenCourseWare UPM