Mesa, M.C.; Oliete Terraz, Patricia Beatriz; Pastor Caño, Jose Ignacio; Martin Sanz, Antonia y Llorca Martinez, Francisco Javier (2014). Mechanical properties up to 1900 K of Al2O3/Er3Al5O12/ZrO2 eutectic ceramics grown by the laser floating zone method. "Journal of the European Ceramic Society", v. 34 (n. 9); pp. 2081-2087. ISSN 0955-2219. https://doi.org/10.1016/j.jeurceramsoc.2013.11.013.

Descripción

Título: Mechanical properties up to 1900 K of Al2O3/Er3Al5O12/ZrO2 eutectic ceramics grown by the laser floating zone method
Autor/es:
  • Mesa, M.C.
  • Oliete Terraz, Patricia Beatriz
  • Pastor Caño, Jose Ignacio
  • Martin Sanz, Antonia
  • Llorca Martinez, Francisco Javier
Tipo de Documento: Artículo
Título de Revista/Publicación: Journal of the European Ceramic Society
Fecha: Agosto 2014
Volumen: 34
Materias:
Palabras Clave Informales: Al2O3/Er3Al5O12/ZrO2; Directionally solidified eutectic ceramics; Mechanical properties; High temperature
Escuela: E.T.S.I. Caminos, Canales y Puertos (UPM)
Departamento: Ciencia de los Materiales
Licencias Creative Commons: Reconocimiento - Sin obra derivada - No comercial

Texto completo

[img]
Vista Previa
PDF (Document Portable Format) - Se necesita un visor de ficheros PDF, como GSview, Xpdf o Adobe Acrobat Reader
Descargar (1MB) | Vista Previa

Resumen

Directionally solidified Al2O3–Er3Al5O12–ZrO2 eutectic rods were processed using the laser floating zone method at growth rates of 25, 350and 750 mm/h to obtain microstructures with different domain size. The mechanical properties were investigated as a function of the processing rate. The hardness, 15.6 GPa, and the fracture toughness, 4 MPa m1/2, obtained from Vickers indentation at room temperature were practically independent of the size of the eutectic phases. However, the flexural strength increased as the domain size decreased, reaching outstanding strength values close to 3 GPa in the samples grown at 750 mm/h. A high retention of the flexural strength was observed up to 1500 K in the materials processed at 25 and 350 mm/h, while superplastic behaviour was observed at 1700 K in the eutectic rods solidified at the highest rate of 750 mm/h

Más información

ID de Registro: 35457
Identificador DC: http://oa.upm.es/35457/
Identificador OAI: oai:oa.upm.es:35457
Identificador DOI: 10.1016/j.jeurceramsoc.2013.11.013
URL Oficial: http://www.sciencedirect.com/science/article/pii/S0955221913005190
Depositado por: Memoria Investigacion
Depositado el: 11 Jun 2015 18:04
Ultima Modificación: 11 Jun 2015 18:04
  • Open Access
  • Open Access
  • Sherpa-Romeo
    Compruebe si la revista anglosajona en la que ha publicado un artículo permite también su publicación en abierto.
  • Dulcinea
    Compruebe si la revista española en la que ha publicado un artículo permite también su publicación en abierto.
  • Recolecta
  • e-ciencia
  • Observatorio I+D+i UPM
  • OpenCourseWare UPM