Comparation Between Pulsed Nd: Yag Laser Superficial Treatment and Ceramic Coating in Creep Test of Ti-6aAl-4V Alloy

Reis, Adriano G.; Reis, Danieli A.P.; Moura Neto, C.; Oñoro Lopez, Javier; Oliveira, H.S. y Couto, A.A. (2010). Comparation Between Pulsed Nd: Yag Laser Superficial Treatment and Ceramic Coating in Creep Test of Ti-6aAl-4V Alloy. "Materials Science Forum", v. 660-66 ; pp. 229-234. ISSN 0255-5476. https://doi.org/10.4028/www.scientific.net/MSF.660-661.229.

Descripción

Título: Comparation Between Pulsed Nd: Yag Laser Superficial Treatment and Ceramic Coating in Creep Test of Ti-6aAl-4V Alloy
Autor/es:
  • Reis, Adriano G.
  • Reis, Danieli A.P.
  • Moura Neto, C.
  • Oñoro Lopez, Javier
  • Oliveira, H.S.
  • Couto, A.A.
Tipo de Documento: Artículo
Título de Revista/Publicación: Materials Science Forum
Fecha: Octubre 2010
Volumen: 660-66
Materias:
Escuela: E.T.S.I. Industriales (UPM)
Departamento: Ingeniería y Ciencia de los Materiales [hasta 2014]
Licencias Creative Commons: Reconocimiento - Sin obra derivada - No comercial

Texto completo

[img]
Vista Previa
PDF (Document Portable Format) - Se necesita un visor de ficheros PDF, como GSview, Xpdf o Adobe Acrobat Reader
Descargar (310kB) | Vista Previa

Resumen

The objective of this work was evaluating the creep resistance of the Ti-6Al-4V alloy with superficial treatment of pulsed Nd:YAG laser and ceramic coating in creep test of Ti-6Al-4V alloy. It was used Ti-6Al-4V alloy as cylindrical bars under forged and annealing of 190oC by 6 hours condition and cooled by air. The Ti-6Al-4V alloy after the superficial treatment of pulsed Nd:YAG laser and ceramic coating was submitted to creep tests at 600°C and 125 at 319 MPa, under constant load mode. In the Nd:YAG pulsed laser treatment was used an environment of 40 % N and 60 % Ar, with 2.1 W of power and 10 m/s of speed. Yttria (8 wt.%) stabilized zirconia (YSZ) with a CoNiCrAlY bond coat was atmospherically plasma sprayed on Ti-6Al-4V substrates by Sulzer Metco Type 9 MB. The obtained results suggest the laser treatment on Ti-6Al-4V alloy improved its creep resistance.

Más información

ID de Registro: 6805
Identificador DC: http://oa.upm.es/6805/
Identificador OAI: oai:oa.upm.es:6805
Identificador DOI: 10.4028/www.scientific.net/MSF.660-661.229
URL Oficial: http://www.scientific.net/MSF.660-661.229
Depositado por: Memoria Investigacion
Depositado el: 03 May 2011 09:06
Ultima Modificación: 20 Abr 2016 15:57
  • Open Access
  • Open Access
  • Sherpa-Romeo
    Compruebe si la revista anglosajona en la que ha publicado un artículo permite también su publicación en abierto.
  • Dulcinea
    Compruebe si la revista española en la que ha publicado un artículo permite también su publicación en abierto.
  • Recolecta
  • e-ciencia
  • Observatorio I+D+i UPM
  • OpenCourseWare UPM